Method for purifying reclaimed polyethylene

ABSTRACT

A method for purifying a reclaimed polyethylene is provided. The method involves obtaining reclaimed polyethylene, contacting it with a first fluid solvent to produce an extracted reclaimed polyethylene then dissolving the extracted reclaimed polyethylene in a solvent to produce a first solution comprising polyethylene and suspended contaminants. The first solution is settled to produce a second solution comprising polyethylene and remaining contaminants. The second solution is purified by contacting the second solution with solid media to produce a third solution comprising purer polyethylene. Finally, the purer polyethylene is separated from the third solution.

FIELD OF THE INVENTION

The present invention generally relates to a method for purifying contaminated polymers through the use of a pressurized solvent and solid media. More specifically, this invention relates to a method for purifying recycled polymers, such as post-consumer and post-industrial recycled plastics, to produce a colorless or clear, odor free, virgin-like polymer. It is particularly useful for the purification of polyethylene.

BACKGROUND OF THE INVENTION

Polymers, especially synthetic plastics, are ubiquitous in daily life due to their relatively low production costs and good balance of material properties. Synthetic plastics are used in a wide variety of applications, such as packaging, automotive components, medical devices, and consumer goods. To meet the high demand of these applications, tens of billions of pounds of synthetic plastics are produced globally on an annual basis. The overwhelming majority of synthetic plastics are produced from increasingly scarce fossil sources, such as petroleum and natural gas. Additionally, the manufacturing of synthetic plastics from fossil sources produces CO₂ as a by-product.

The ubiquitous use of synthetic plastics has consequently resulted in millions of tons of plastic waste being generated every year. While the majority of plastic waste is landfilled via municipal solid waste programs, a significant portion of plastic waste is found in the environment as litter, which is unsightly and potentially harmful to ecosystems. Plastic waste is often washed into river systems and ultimately out to sea.

Plastics recycling has emerged as one solution to mitigate the issues associated with the wide-spread usage of plastics. Recovering and re-using plastics diverts waste from landfills and reduces the demand for virgin plastics made from fossil-based resources, which consequently reduces greenhouse gas emissions. In developed regions, such as the United States and the European Union, rates of plastics recycling are increasing due to greater awareness by consumers, businesses, and industrial manufacturing operations. The majority of recycled materials, including plastics, are mixed into a single stream which is collected and processed by a material recovery facility (MRF). At the MRF, materials are sorted, washed, and packaged for resale. Plastics can be sorted into individual materials, such as high-density polyethylene (HDPE) or poly(ethylene terephthalate) (PET), or mixed streams of other common plastics, such as polypropylene (PP), low-density polyethylene (LDPE), poly(vinyl chloride) (PVC), polystyrene (PS), polycarbonate (PC), and polyamides (PA). The single or mixed streams can then be further sorted, washed, and reprocessed into a pellet that is suitable for re-use in plastics processing, for example blow and injection molding.

Though recycled plastics are sorted into predominately uniform streams and are washed with aqueous and/or caustic solutions, the final reprocessed pellet often remains highly contaminated with unwanted waste impurities, such as spoiled food residue and residual perfume components. In addition, recycled plastic pellets, except for those from recycled beverage containers, are darkly colored due to the mixture of dyes and pigments commonly used to colorize plastic articles. While there are some applications that are insensitive to color and contamination (for example black plastic paint containers and concealed automotive components), the majority of applications require non-colored pellets. The need for high quality, “virgin-like” recycled resin is especially important for food and drug contact applications, such as food packaging. In addition to being contaminated with impurities and mixed colorants, many recycled resin products are often heterogeneous in chemical composition and may contain a significant amount of polymeric contamination, such as recycled polypropylene contamination in polyethylene and vice versa.

Mechanical recycling, also known as secondary recycling, is the process of converting recycled plastic waste into a re-usable form for subsequent manufacturing. A more detailed review of mechanical recycling and other plastics recovery processes are described in S. M. Al-Salem, P. Lettieri, J. Baeyens, “Recycling and recovery routes of plastic solid waste (PSW): A review”, Waste Management, Volume 29, Issue 10, October 2009, Pages 2625-2643, ISSN 0956-053X. While advances in mechanical recycling technology have improved the quality of recycled polymers to some degree, there are fundamental limitations of mechanical decontamination approaches, such as the physical entrapment of pigments within a polymer matrix. Thus, even with the improvements in mechanical recycling technology, the dark color and high levels of chemical contamination in currently available recycled plastic waste prevents broader usage of recycled resins by the plastics industry.

To overcome the fundamental limitations of mechanical recycling, there have been many methods developed to purify contaminated polymers via chemical approaches, or chemical recycling. Most of these methods use solvents to decontaminate and purify polymers. The use of solvents enables the extraction of impurities and the dissolution of polymers, which further enables alternative separation technologies.

For example, U.S. Pat. No. 7,935,736 describes a method for recycling polyester from polyester-containing waste using a solvent to dissolve the polyester prior to cleaning. The '736 patent also describes the need to use a precipitant to recover the polyester from the solvent.

In another example, U.S. Pat. No. 6,555,588 describes a method to produce a polypropylene blend from a plastic mixture comprised of other polymers. The '588 patent describes the extraction of contaminants from a polymer at a temperature below the dissolution temperature of the polymer in the selected solvent, such as hexane, for a specified residence period. The '588 patent further describes increasing the temperature of the solvent (or a second solvent) to dissolve the polymer prior to filtration. The '588 patent yet further describes the use of shearing or flow to precipitate polypropylene from solution. The polypropylene blend described in the '588 patent contained polyethylene contamination up to 5.6 wt %.

In another example, European Patent Application No. 849,312 (translated from German to English) describes a process to obtain purified polyolefins from a polyolefin-containing plastic mixture or a polyolefin-containing waste. The '312 patent application describes the extraction of polyolefin mixtures or wastes with a hydrocarbon fraction of gasoline or diesel fuel with a boiling point above 90° C. at temperatures between 90° C. and the boiling point of the hydrocarbon solvent. The '312 patent application further describes contacting a hot polyolefin solution with bleaching clay and/or activated carbon to remove foreign components from the solution. The '312 patent yet further describes cooling the solution to temperatures below 70° C. to crystallize the polyolefin and then removing adhering solvent by heating the polyolefin above the melting point of the polyolefin, or evaporating the adhering solvent in a vacuum or passing a gas stream through the polyolefin precipitate, and/or extraction of the solvent with an alcohol or ketone that boils below the melting point of the polyolefin.

In another example, U.S. Pat. No. 5,198,471 describes a method for separating polymers from a physically commingled solid mixture (for example waste plastics) containing a plurality of polymers using a solvent at a first lower temperature to form a first single phase solution and a remaining solid component. The '471 patent further describes heating the solvent to higher temperatures to dissolve additional polymers that were not solubilized at the first lower temperature. The '471 patent describes filtration of insoluble polymer components.

In another example, U.S. Pat. No. 5,233,021 describes a method of extracting pure polymeric components from a multi-component structure (for example waste carpeting) by dissolving each component at an appropriate temperature and pressure in a supercritical fluid and then varying the temperature and/or pressure to extract particular components in sequence. However, similar to the '471 patent, the '021 patent only describes filtration of undissolved components.

In another example, U.S. Pat. No. 5,739,270 describes a method and apparatus for continuously separating a polymer component of a plastic from contaminants and other components of the plastic using a co-solvent and a working fluid. The co-solvent at least partially dissolves the polymer and the second fluid (that is in a liquid, critical, or supercritical state) solubilizes components from the polymer and precipitates some of the dissolved polymer from the co-solvent. The '270 patent further describes the step of filtering the thermoplastic-co-solvent (with or without the working fluid) to remove particulate contaminants, such as glass particles.

The known solvent-based methods to purify contaminated polymers, as described above, do not produce “virgin-like” polymer. In the previous methods, co-dissolution and thus cross contamination of other polymers often occurs. If adsorbent is used, a filtration and/or centrifugation step is often employed to remove the used adsorbent from solution. In addition, isolation processes to remove solvent, such as heating, vacuum evaporation, and/or precipitation using a precipitating chemical are used to produce a polymer free of residual solvent.

Accordingly, a need still exists for an improved solvent-based method to purify contaminated polymers that uses a solvent that is readily and economically removed from the polymer, is relatively simple in terms of the number of unit operations, produces a polymer without a significant amount of polymeric cross contamination, produces a polymer that is essentially colorless, and produces a polymer that is essentially odorless.

SUMMARY OF THE INVENTION

A method for purifying a reclaimed polyethylene is provided. The method involves:

-   -   a. Obtaining reclaimed polyethylene selected from the group         consisting of post-consumer use polymers, post-industrial use         polymers, and combinations thereof;     -   b. Contacting the reclaimed polyethylene at a temperature from         about 80° C. to about 220° C. and at a pressure from about 150         psig (1.03 MPa) to about 15,000 psig (103.42 MPa) with a first         fluid solvent having a standard boiling point less than about         70° C., to produce an extracted reclaimed polyethylene;     -   c. Dissolving the extracted reclaimed polyethylene in a solvent         selected from the group consisting of the first fluid solvent, a         second fluid solvent, and mixtures thereof, at a temperature         from about 90° C. to about 220° C. and a pressure from about 350         psig (2.41 MPa) to about 20,000 psig (137.90 MPa) to produce a         first solution comprising polyethylene and suspended         contaminants;     -   d. Settling the first solution comprising polyethylene and         suspended contaminants at a temperature from about 90° C. to         about 220° C. and at a pressure from about 350 psig (2.41 MPa)         to about 20,000 psig (137.90 MPa) to produce a second solution         comprising polyethylene and remaining contaminants;     -   e. Purifying the second solution at a temperature from about         90° C. to about 220° C. and at a pressure from about 350 psig         (2.41 MPa) to about 20,000 psig (137.90 MPa) by contacting the         second solution with solid media to produce a third solution         comprising purer polyethylene; and     -   f. Separating the purer polyethylene from the third solution.         The second fluid solvent may have either the same chemical         composition or a different chemical composition than the first         fluid solvent.

In one embodiment, the polyethylene is separated from the third solution at a temperature from about 0° C. to about 220° C. and a pressure from about 0 psig (0 MPa) to 2,000 psig (13.79 MPa). In another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 0.5%. In yet another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 1%. In one embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 2%.

In one embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 3%. In another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 4%. In yet another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 5%.

In one embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 20%. In another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 18%. In yet another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 16%. In one embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 14%. In another embodiment, the reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 12%.

In one embodiment, the reclaimed polyethylene is post-consumer recycle derived polyethylene. In another embodiment, the reclaimed polyethylene is a polyethylene homopolymer or a primarily polyethylene copolymer. In yet another embodiment, the fluid solvent has a standard boiling point less than about 0° C. and greater than about −45° C. and a standard enthalpy change of vaporization of less than about +25 kJ/mol.

In one embodiment, the fluid solvent is selected from the group consisting of olefinic hydrocarbons, aliphatic hydrocarbons, and mixtures thereof. In another embodiment, the aliphatic hydrocarbon is selected from the group consisting of C₁-C₆ aliphatic hydrocarbons and mixtures thereof. In yet another embodiment, the aliphatic hydrocarbons and mixtures thereof is comprised of primarily C₄ aliphatic hydrocarbons.

In another embodiment, the fluid solvent consists essentially of C₄ liquefied petroleum gas. In one embodiment, the fluid solvent is n-butane, butane isomers, or mixtures thereof. In another embodiment, the temperature in the contacting, dissolving, settling and purification steps is from about 110° C. to about 170° C.

In one embodiment, the pressure in the contacting step is from about 1,100 psig (7.58 MPa) to about 5,500 psig (37.92 MPa). In another embodiment, the pressure in the contacting step is less than about 1,100 psig (7.58 MPa). In yet another embodiment, the pressure in the dissolving, settling, and purification steps is greater than about 4,500 psig (31.03 MPa). In one embodiment, the pressure in the dissolving, settling, and purification steps is greater than about 5,500 psig (37.92 MPa).

In one embodiment, the solid media is selected from the group consisting of inorganic substances, carbon-based substances, and mixtures thereof. In another embodiment, the inorganic substances are selected from the group consisting of oxides of silicon, oxides of aluminum, oxides of iron, aluminum silicates, amorphous volcanic glasses, and mixtures thereof. In yet another embodiment, the inorganic substances are selected from the group consisting of silica gel, diatomite, sand, quartz, alumina, perlite, fuller's earth, bentonite, and mixtures thereof.

In one embodiment, the carbon-based substances are selected from the group consisting of anthracite coal, carbon black, coke, activated carbon, cellulose, and mixtures thereof. In another embodiment, the contacting of the polyethylene solution with said solid media is done in a packed bed of said solid media. In yet another embodiment, the packed bed is greater than 20 cm in length.

Additional features of the invention may become apparent to those skilled in the art from a review of the following detailed description, taken in conjunction with the examples.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a block flow diagram showing the major steps of one embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION I. Definitions

As used herein, the term “reclaimed polymer” refers to a polymer used for a previous purpose and then recovered for further processing.

As used herein, the term “reclaimed polyethylene” refers to a polyethylene polymer used for a previous purpose and then recovered for further processing.

As used herein, the term “post-consumer” refers to a source of material that originates after the end consumer has used the material in a consumer good or product.

As used herein, the term “post-consumer recycle” (PCR) refers to a material that is produced after the end consumer has used the material and has disposed of the material in a waste stream.

As used herein, the term “post-industrial” refers to a source of a material that originates during the manufacture of a good or product.

As used herein, the term “fluid solvent” refers to a substance that may exist in the liquid state under specified conditions of temperature and pressure. In some embodiments the fluid solvent may be a predominantly homogenous chemical composition of one molecule or isomer, while in other embodiments, the fluid solvent may be a mixture of several different molecular compositions or isomers. Further, in some embodiments of the present invention, the term “fluid solvent” may also apply to substances that are at, near, or above the critical temperature and critical pressure (critical point) of that substance. It is well known to those having ordinary skill in the art that substances above the critical point of that substance are known as “supercritical fluids” which do not have the typical physical properties (i.e. density) of a liquid.

As used herein, the term “dissolved” means at least partial incorporation of a solute (polymeric or non-polymeric) in a solvent at the molecular level. Further, the thermodynamic stability of the solute/solvent solution can be described by the following equation 1: ΔG _(mix) =ΔH _(m) −TΔS _(mix)  Equation 1

where ΔG_(mix) is the Gibbs free energy change of mixing of a solute with a solvent, ΔH_(mix) is the enthalpy change of mixing, T is the absolute temperature, and ΔS_(mix) is the entropy of mixing. To maintain a stable solution of a solute in a solvent, the Gibbs free energy must be negative and at a minimum. Thus, any combination of solute and solvent that minimize a negative Gibbs free energy at appropriate temperatures and pressures can be used for the present invention.

As used herein, the term “standard boiling point” refers to the boiling temperature at an absolute pressure of exactly 100 kPa (1 bar, 14.5 psia, 0.9869 atm) as established by the International Union of Pure and Applied Chemistry (IUPAC).

As used herein, the term “standard enthalpy change of vaporization” refers to the enthalpy change required to transform a specified quantity of a substance from a liquid into a vapor at the standard boiling point of the substance.

As used herein, the term “polyethylene solution” refers to a solution of polyethylene dissolved in a solvent. The polyethylene solution may contain undissolved matter and thus the polyethylene solution may also be a “slurry” of undissolved matter suspended in a solution of polyethylene dissolved in a solvent.

As used herein, the terms “sedimentation” and “settling” refer to the tendency of particles within a suspension to separate from a liquid in response to a force (typically a gravitational force) acting upon the particles.

As used herein, the term “suspended contaminants” refers to unwanted or undesired constituents that are present throughout the bulk of medium of a heterogeneous mixture.

As used herein, the term “solid media” refers to a substance that exists in the solid state under the conditions of use. The solid media may be crystalline, semi-crystalline, or amorphous. The solid media may be granular and may be supplied in different shapes (i.e. spheres, cylinders, pellets, etc.). If the solid media is granular, the particle size and particle size distribution of solid media may be defined by the mesh size used to classify the granular media. An example of standard mesh size designations can be found in the American Society for Testing and Material (ASTM) standard ASTM E11 “Standard Specification for Woven Wire Test Sieve Cloth and Test Sieves.” The solid media may also be a non-woven fibrous mat or a woven textile.

As used herein, the term “purer polyethylene solution” refers to a polyethylene solution having fewer contaminants relative to the same polyethylene solution prior to a purification step.

As used herein, the term “extraction” refers to the practice of transferring a solute species from a liquid phase (or solid matrix) across a phase boundary to a separate immiscible liquid phase. The driving force(s) for extraction are described by partition theory.

As used herein, the term “extracted” refers to a material having fewer solute species relative to the same material prior to an extraction step. As used herein, the term “extracted reclaimed polyethylene” refers to a reclaimed polyethylene having fewer solute species relative to the same reclaimed polyethylene prior to an extraction step.

As used herein, the term “virgin-like” means essentially contaminant-free, pigment-free, odor-free, homogenous, and similar in properties to virgin polymers.

As used herein, the term “primarily polyethylene copolymer” refers a copolymer with greater than 70 mol % of ethylene repeating units.

As used herein, any reference to international units of pressure (e.g. MPa) refers to gauge pressure.

II. Method for Purifying Contaminated Polyethylene

Surprisingly, it has been found that certain fluid solvents, which in a preferred embodiment exhibit temperature and pressure-dependent solubility for polymers, when used in a relatively simple process can be used to purify contaminated polyethylene, especially reclaimed or recycled polyethylene, to a near virgin-like quality. This process, exemplified in FIG. 1, comprises 1) obtaining a reclaimed polyethylene (step a in FIG. 1), followed by 2) extracting the polyethylene with a fluid solvent at an extraction temperature (T_(E)) and at an extraction pressure (P_(E)) (step b in FIG. 1), followed by 3) dissolution of the polyethylene in a fluid solvent at a dissolution temperature (T_(D)) and at a dissolution pressure (P_(D)) (step c in FIG. 1), followed by 4) sedimentation of the polymer solution at a dissolution temperature (T_(D)) and at a dissolution pressure (P_(D)) (step d in FIG. 1), followed by 5) contacting the dissolved polyethylene solution with solid media at a dissolution temperature (T_(D)) and at a dissolution pressure (P_(D)) (step e in FIG. 1), followed by separation of the polyethylene from the fluid solvent (step f in FIG. 1).

In one embodiment of the present invention, the purified polyethylene, which may be sourced from post-consumer waste streams, is essentially contaminant-free, pigment-free, odor-free, homogenous, and similar in properties to virgin polymers. Furthermore, in a preferred embodiment, the physical properties of the fluid solvent of the present invention may enable more energy efficient methods for separation of the fluid solvent from the purified polyethylene.

Reclaimed Polyethylene

In one embodiment of the present invention, a method for purifying reclaimed polyethylene includes obtaining reclaimed polyethylene. For the purposes of the present invention, the reclaimed polyethylene is sourced from post-consumer, post-industrial, post-commercial, and/or other special waste streams. For example, post-consumer waste polyethylene can be derived from curbside recycle streams where end-consumers place used polymers from packages and products into a designated bin for collection by a waste hauler or recycler. Post-consumer waste polymers can also be derived from in-store “take-back” programs where the consumer brings waste polymers into a store and places the waste polymers in a designated collection bin. An example of post-industrial waste polymers can be waste polymers produced during the manufacture or shipment of a good or product that are collected as unusable material by the manufacturer (i.e. trim scraps, out of specification material, start up scrap). An example of waste polymers from a special waste stream can be waste polymers derived from the recycling of electronic waste, also known as “e-waste.” Another example of waste polymers from a special waste stream can be waste polymers derived from the recycling of automobiles. Another example of waste polymers from a special waste stream can be waste polymers derived from the recycling of used carpeting and textiles.

For the purposes of the present invention, the reclaimed polyethylene is a homogenous composition of an individual polymer or a mixture of several different polyethylene compositions. Non-limiting examples of polyethylene compositions are homopolymers and copolymers of ethylene, such as high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), copolymers of ethylene and alpha-olefins, and other dissolvable polyethylene polymers that may be apparent to those having ordinary skill in the art.

The reclaimed polyethylene may also contain various pigments, dyes, process aides, stabilizing additives, fillers, and other performance additives that were added to the polymer during polymerization or conversion of the original polymer to the final form of an article. Non-limiting examples of pigments are organic pigments, such as copper phthalocyanine, inorganic pigments, such as titanium dioxide, and other pigments that may be apparent to those having ordinary skill in the art. A non-limiting example of an organic dye is Basic Yellow 51. Non-limiting examples of process aides are antistatic agents, such as glycerol monostearate and slip-promoting agents, such as erucamide. A non-limiting example of a stabilizing additive is octadecyl-3-(3,5-di-tert.butyl-4-hydroxyphenyl)-propionate. Non-limiting examples of fillers are calcium carbonate, talc, and glass fibers.

Solvent

The fluid solvent of the present invention has a standard boiling point less than about 70° C. Pressurization maintains solvents, which have standard boiling points below the operating temperature range of the present invention, in a state in which there is little or no solvent vapor. In one embodiment, the fluid solvent with a standard boiling point less than about 70° C. is selected from the group consisting of carbon dioxide, ketones, alcohols, ethers, esters, alkenes, alkanes, and mixtures thereof. Non-limiting examples of fluid solvents with standard boing points less than about 70° C. are carbon dioxide, acetone, methanol, dimethyl ether, diethyl ether, ethyl methyl ether, tetrahydrofuran, methyl acetate, ethylene, propylene, 1-butene, 2-butene, isobutylene, 1-pentene, 2-pentene, branched isomers of pentene, 1-hexene, 2-hexene, methane, ethane, propane, n-butane, isobutane, n-pentane, isopentane, neopentane, n-hexane, isomers of isohexane, and other substances that may be apparent to those having ordinary skill in the art.

The selection of the fluid solvent used will dictate the temperature and pressure ranges used to perform the steps of the present invention. A review of polymer phase behavior in solvents of the kind described by the present invention is provided in the following reference: McHugh et al. (1999) Chem. Rev. 99:565-602.

Extraction

In one embodiment of the present invention, a method for purifying polyethylene includes contacting reclaimed polyethylene with a fluid solvent at a temperature and at a pressure wherein the polymer is essentially insoluble in the fluid solvent. Although not wishing to be bound by any theory, applicants believe that the temperature and pressure-dependent solubility can be controlled in such a way to prevent the fluid solvent from fully solubilizing the polymer, however, the fluid solvent can diffuse into the polymer and extract any extractable contamination. The extractable contamination may be residual processing aides added to the polymer, residual product formulations which contacted the polymer, such as perfumes and flavors, dyes, and any other extractable material that may have been intentionally added or unintentionally became incorporated into the polymer, for example, during waste collection and subsequent accumulation with other waste materials.

In one embodiment, the controlled extraction may be accomplished by fixing the temperature of the polymer/fluid solvent system and then controlling the pressure below a pressure, or pressure range, where the polymer dissolves in the fluid solvent. In another embodiment, the controlled extraction is accomplished by fixing the pressure of the polymer/solvent system and then controlling the temperature below a temperature, or temperature range where the polymer dissolves in the fluid solvent. The temperature and pressure-controlled extraction of the polymer with a fluid solvent uses a suitable pressure vessel and may be configured in a way that allows for continuous extraction of the polymer with the fluid solvent. In one embodiment of the present invention, the pressure vessel may be a continuous liquid-liquid extraction column where molten polymer is pumped into one end of the extraction column and the fluid solvent is pumped into the same or the opposite end of the extraction column. In another embodiment, the fluid containing extracted contamination is removed from the process. In another embodiment, the fluid containing extracted contamination is purified, recovered, and recycled for use in the extraction step or a different step in the process. In one embodiment of the present invention, the extraction may be performed as a batch method, wherein the reclaimed polyethylene is fixed in a pressure vessel and the fluid solvent is continuously pumped through the fixed polymer phase. The extraction time or the amount of fluid solvent used will depend on the desired purity of the final purer polymer and the amount of extractable contamination in the starting reclaimed polyethylene. In another embodiment, the fluid containing extracted contamination is contacted with solid media in a separate step as described in the “Purification” section below. In another embodiment, a method for purifying reclaimed polyethylene includes contacting reclaimed polyethylene with a fluid solvent at a temperature and at a pressure wherein the polymer is molten and in the liquid state. In another embodiment, the reclaimed polyethylene is contacted with the fluid solvent at a temperature and at a pressure wherein the polymer is in the solid state.

In one embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with a fluid solvent at a temperature and a pressure wherein the polyethylene remains essentially undissolved. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with n-butane at a temperature from about 80° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with n-butane at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with n-butane at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with n-butane at a pressure from about 150 psig (1.03 MPa) to about 6,500 psig (44.82 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with n-butane at a pressure from about 3,000 psig (20.68 MPa) to about 6,000 psig (41.37 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with n-butane at a pressure from about 4,500 psig (31.03 MPa) to about 5,500 psig (37.92 MPa).

In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with propane at a temperature from about 80° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with propane at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with propane at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with propane at a pressure from about 1,000 psig (6.89 MPa) to about 15,000 psig (103.42 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with propane at a pressure from about 2,000 psig (13.79 MPa) to about 10,000 psig (68.95 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting polyethylene with propane at a pressure from about 5,000 psig (34.47 MPa) to about 9,000 psig (62.05 MPa).

Dissolution

In one embodiment of the present invention, a method for purifying reclaimed polyethylene includes dissolving the reclaimed polyethylene in a fluid solvent at a temperature and at a pressure wherein the polymer is dissolved in the fluid solvent. Although not wishing to be bound by any theory, applicants believe that the temperature and pressure can be controlled in such a way to enable thermodynamically favorable dissolution of the reclaimed polymer in a fluid solvent. Furthermore, the temperature and pressure can be controlled in such a way to enable dissolution of a particular polymer or polymer mixture while not dissolving other polymers or polymer mixtures. This controllable dissolution enables the separation of polymers from polymer mixtures.

In one embodiment of the present invention, a method for purifying polymers includes dissolving contaminated reclaimed polyethylene in a solvent that does not dissolve the contaminants under the same conditions of temperature and pressure. The contaminants may include pigments, fillers, dirt, and other polymers. These contaminants are released from the reclaimed polyethylene upon dissolution and then removed from the polymer solution via a subsequent solid-liquid separation step.

In one embodiment of the present invention, a method for purifying reclaimed polyethylene includes dissolving polyethylene in a fluid solvent at a temperature and at a pressure wherein the polyethylene is dissolved in the fluid solvent. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a temperature from about 90° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a pressure from about 1,000 psig (6.89 MPa) to about 12,000 psig (82.74 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a pressure from about 2,000 psig (13.79 MPa) to about 10,000 psig (68.95 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a pressure from about 4,000 psig (27.58 MPa) to about 6,000 psig (41.37 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a mass percent concentration of at least 0.5%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 1%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 2%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 3%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 4%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 5%. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in n-butane at a mass percent concentration up to 20%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 18%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 16%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 14%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 12%.

In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a temperature from about 90° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a pressure from about 3,000 psig (20.68 MPa) to about 20,000 psig (137.90 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a pressure from about 5,000 psig (34.47 MPa) to about 15,000 psig (103.42 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a pressure from about 8,000 psig (55.16 MPa) to about 11,000 psig (75.84 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a mass percent concentration of at least 0.5%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 1%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 2%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 3%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 4%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 5%. In another embodiment, a method for purifying reclaimed polyethylene includes dissolving polyethylene in propane at a mass percent concentration up to 20%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 18%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 16%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 14%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 12%.

Sedimentation

In one embodiment of the present invention, a method for purifying polyethylene includes separating the undissolved contaminants from the polyethylene solution via a sedimentation (also known as settling) step at a temperature and at a pressure wherein the polymer remains dissolved in the fluid solvent. In one embodiment, the settling step causes the undissolved contaminants to experience a force that uniformly moves the undissolved contaminants in the direction of the force. Typically the applied settling force is gravity, but can also be a centrifugal, centripetal, or some other force. The amount of applied force and duration of settling time will depend upon several parameters, including, but not limited to: particle size of the contaminant particles, contaminant particle densities, density of the fluid or solution, and the viscosity of the fluid or solution. The following equation (equation 2) is a relationship between the aforementioned parameters and the settling velocity, which is a measure of the contaminant sedimentation rate:

$\begin{matrix} {v = \frac{2\left( {\rho_{p} - \rho_{f}} \right)g\; r^{2}}{9\eta}} & {{Equation}\mspace{14mu} 2} \end{matrix}$

where ν is the settling velocity, ρ_(p) is the density of the contaminant particle, ρ_(f) is the density of the fluid or solution, g is the acceleration due to the applied force (typically gravity), r is the radius of the contaminant particle and η is the dynamic viscosity of the fluid or solution. Some of the key parameters that determine the solution viscosity are: the chemical composition of the fluid solvent, the molecular weight of the polymer dissolved in the fluid solvent, the concentration of dissolved polymer in the fluid solvent, the temperature of the fluid solvent solution, and the pressure of the fluid solvent solution.

In one embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/fluid solvent solution at a temperature and at a pressure wherein the polyethylene remains dissolved in the fluid solvent. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution at a temperature from about 90° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution at a pressure from about 1,000 psig (6.89 MPa) to about 12,000 psig (82.74 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution at a pressure about 2,000 psig (13.79 MPa) to about 10,000 psig (68.95 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution at a pressure from about 4,000 psig (27.58 MPa) to about 6,000 psig (41.37 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution wherein the polyethylene is dissolved at a mass percent concentration of at least 0.5%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 1%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 2%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 3%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 4%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 5%. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/n-butane solution where in the polyethylene is dissolved at a mass percent concentration up to 20%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 18%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 16%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 14%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 12%.

In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution at a temperature from about 90° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution with at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution at a pressure from about 3,000 psig (20.68 MPa) to about 20,000 psig (137.90 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution at a pressure from about 5,000 psig (34.47 MPa) to about 15,000 psig (103.42 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution with at a pressure from about 8,000 psig (55.16 MPa) to about 11,000 psig (75.84 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution wherein the polyethylene is dissolved at a mass percent concentration of at least 0.5%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 1%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 2%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 3%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 4%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 5%. In another embodiment, a method for purifying reclaimed polyethylene includes settling contaminants from a polyethylene/propane solution where in the polyethylene is dissolved at a mass percent concentration up to 20%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 18%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 16%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 14%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 12%.

Purification

In one embodiment of the present invention, a method for purifying polyethylene includes contacting a contaminated polymer solution with solid media at a temperature and at a pressure wherein the polymer remains dissolved in the fluid solvent. The solid media of the present invention is any solid material that removes at least some of the contamination from a solution of reclaimed polyethylene dissolved in the fluid solvent of the present invention. Although not wishing to be bound by any theory, the applicants believe that the solid media removes contamination by a variety of mechanisms. Non-limiting examples of possible mechanisms include adsorption, absorption, size exclusion, ion exclusion, ion exchange, and other mechanisms that may be apparent to those having ordinary skill in the art. Furthermore, the pigments and other contaminants commonly found in reclaimed polyethylene may be polar compounds and may preferentially interact with the solid media, which may also be at least slightly polar. The polar-polar interactions are especially favorable when non-polar solvents, such as alkanes, are used as the fluid solvent.

In one embodiment of the present invention, the solid media is selected from the group consisting of inorganic substances, carbon-based substances, or mixtures thereof. Useful examples of inorganic substances include oxides of silicon, oxides of aluminum, oxides of iron, aluminum silicates, magnesium silicates, amorphous volcanic glasses, silica, silica gel, diatomite, sand, quartz, reclaimed glass, alumina, perlite, fuller's earth, bentonite, and mixtures thereof. Useful examples of carbon-based substances include anthracite coal, carbon black, coke, activated carbon, cellulose, and mixtures thereof. In another embodiment of the present invention, the solid media is recycled glass.

In one embodiment of the present invention, the solid media is contacted with the polymer in a vessel for a specified amount of time while the solid media is agitated. In another embodiment, the solid media is removed from the purer polymer solution via a solid-liquid separation step. Non-limiting examples of solid-liquid separation steps include filtration, decantation, centrifugation, and settling. In another embodiment of the present invention, the contaminated polymer solution is passed through a stationary bed of solid media. In another embodiment of the present invention, the height or length of the stationary bed of solid media is greater than 5 cm. In another embodiment of the present invention, the height or length of the stationary bed of solid media is greater than 10 cm. In another embodiment of the present invention, the height or length of the stationary bed of solid media is greater than 20 cm. In another embodiment of the present invention, the solid media is replaced as needed to maintain a desired purity of polymer. In yet another embodiment, the solid media is regenerated and re-used in the purification step. In another embodiment, the solid media is regenerated by fluidizing the solid media during a backwashing step.

In one embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/fluid solvent solution with solid media at a temperature and a pressure wherein the polyethylene remains dissolved in the fluid solvent. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media at a temperature from about 90° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media at a pressure from about 1,000 psig (6.89 MPa) to about 12,000 psig (82.74 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media at a pressure from about 2,000 psig (13.79 MPa) to about 10,000 psig (68.95 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media at a pressure from about 4,000 psig (27.58 MPa) to about 6,000 psig (41.37 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media wherein the polyethylene is dissolved at a mass percent concentration of at least 0.5%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 1%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 2%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 3%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 4%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 5%. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/n-butane solution with solid media wherein the polyethylene is dissolved at a mass percent concentration up to 20%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 18%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 16%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 14%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 12%.

In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media at a temperature from about 90° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media at a temperature from about 100° C. to about 200° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media at a temperature from about 130° C. to about 180° C. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media at a pressure from about 3,000 psig (20.68 MPa) to about 20,000 psig (137.90 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media at a pressure from about 5,000 psig (34.47 MPa) to about 15,000 psig (103.42 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media at a pressure from about 8,000 psig (55.16 MPa) to about 11,000 psig (75.84 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media wherein the polyethylene is dissolved at a mass percent concentration of at least 0.5%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 1%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 2%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 3%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 4%. In another embodiment, the polyethylene is dissolved at a mass percent concentration of at least 5%. In another embodiment, a method for purifying reclaimed polyethylene includes contacting a polyethylene/propane solution with solid media wherein the polyethylene is dissolved at a mass percent concentration up to 20%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 18%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 16%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 14%. In another embodiment, the polyethylene is dissolved at a mass percent concentration up to 12%.

Separation

In one embodiment of the present invention, a method for purifying reclaimed polyethylene includes separating the purer polymer from the fluid solvent at a temperature and at a pressure wherein the polymer precipitates from solution and is no longer dissolved in the fluid solvent. In another embodiment, the precipitation of the purer polymer from the fluid solvent is accomplished by reducing the pressure at a fixed temperature. In another embodiment, the precipitation of the purer polymer from the fluid solvent is accomplished by reducing the temperature at a fixed pressure. In another embodiment, the precipitation of the purer polymer from the fluid solvent is accomplished by increasing the temperature at a fixed pressure. In another embodiment, the precipitation of the purer polymer from the fluid solvent is accomplished by reducing both the temperature and pressure. The solvent can be partially or completely converted from the liquid to the vapor phase by controlling the temperature and pressure. In another embodiment, the precipitated polymer is separated from the fluid solvent without completely converting the fluid solvent into a 100% vapor phase by controlling the temperature and pressure of the solvent during the separation step. The separation of the precipitated purer polymer is accomplished by any method of liquid-liquid or liquid-solid separation. Non-limiting examples of liquid-liquid or liquid-solid separations include filtration, decantation, centrifugation, and settling.

In one embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/fluid solvent solution at a temperature and a pressure wherein the polyethylene precipitates from solution. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/n-butane solution at a temperature from about 0° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/n-butane solution at a temperature from about 50° C. to about 175° C. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/n-butane solution at a temperature from about 100° C. to about 160° C. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/n-butane solution at a pressure from about 0 psig (0 MPa) to about 4,000 psig (27.58 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/n-butane solution at a pressure from about 50 psig (0.34 MPa) to about 2,000 psig (13.79 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/n-butane solution at a pressure from about 75 psig (0.52 MPa) to about 1,000 psig (6.89 MPa).

In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/propane solution at a temperature from about −42° C. to about 220° C. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/propane solution at a temperature from about 0° C. to about 150° C. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/propane solution at a temperature from about 50° C. to about 130° C. In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/propane solution at a pressure from about 0 psig (0 MPa) to about 15,000 psig (103.42 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/propane solution at a pressure from about 50 psig (0.34 MPa) to about 5,000 psig (34.48 MPa). In another embodiment, a method for purifying reclaimed polyethylene includes separating polyethylene from a polyethylene/propane solution at a pressure from about 75 psig (0.52 MPa) to about 1,000 psig (6.89 MPa).

Every document cited herein, including any cross reference or related patent or patent application, is hereby incorporated herein by reference in its entirety unless expressly excluded or otherwise limited. The citation of any document is not an admission that it is prior art with respect to any invention disclosed or claimed herein or that it alone, or in any combination with any other reference or references, teaches, suggest or discloses any such invention. Further, to the extent that any meaning or definition of a term in this document conflicts with any meaning or definition of the same term in a document incorporated by reference, the meaning or definition assigned to that term in this document shall govern.

While particular embodiments of the present invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modification can be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modification that are within the scope of the present invention. 

What is claimed is:
 1. A method for purifying reclaimed polyethylene comprising: a. Obtaining the reclaimed polyethylene wherein said reclaimed polyethylene is selected from the group consisting of post-consumer use polymers, post-industrial use polymers, and combinations thereof; b. Contacting the reclaimed polyethylene at a temperature from about 80° C. to about 220° C. and ata pressure from about 150 psig (1.03 MPa) to about 15,000 psig (103.42 MPa) with a first fluid solvent having a standard boiling point less than about 70° C., to produce an extracted reclaimed polyethylene; c. Dissolving the extracted reclaimed polyethylene in a solvent selected from the group consisting of the first fluid solvent, a second fluid solvent, and mixtures thereof, at a temperature from about 90° C. to about 220° C. and a pressure from about 350 psig (2.41 MPa) to about 20,000 psig (137.90 MPa) to produce a first solution comprising polyethylene and suspended contaminants; d. Settling said first solution comprising polyethylene and suspended contaminants at a temperature from about 90° C. to about 220° C. and at a pressure from about 350 psig (2.41 MPa) to about 20,000 psig (137.90 MPa) to produce a second solution comprising polyethylene and remaining contaminants; e. Purifying said second solution at a temperature from about 90° C. to about 220° C. and at a pressure from about 350 psig (2.41 MPa) to about 20,000 psig (137.90 MPa) by contacting said second solution with solid media to produce a third solution comprising purer polyethylene; and f. Separating said purer polyethylene from said third solution; wherein said second fluid solvent has the same chemical composition or a different chemical composition as the first fluid solvent.
 2. The method of claim 1, wherein said polyethylene is separated from said third solution at a temperature from about 0° C. to about 220° C. and a pressure from about 0 psig (0 MPa) to 2,000 psig (13.79 MPa).
 3. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 0.5%.
 4. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 1%.
 5. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 2%.
 6. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 3%.
 7. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 4%.
 8. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration of at least 5%.
 9. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 20%.
 10. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 18%.
 11. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 16%.
 12. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 14%.
 13. The method of claim 1, wherein said reclaimed polyethylene is dissolved in the fluid solvent, or fluid solvent mixture, at a mass percent concentration up to 12%.
 14. The method of claim 1, wherein the reclaimed polyethylene is post-consumer recycle derived polyethylene.
 15. The method of claim 1, wherein said polyethylene is a polyethylene homopolymer or a primarily polyethylene copolymer.
 16. The method of claim 1, wherein said fluid solvent has a standard boiling point less than about 0° C. and greater than about −45° C. and a standard enthalpy change of vaporization of less than about +25 kJ/mol.
 17. The method of claim 1, wherein said fluid solvent is selected from the group consisting of olefinic hydrocarbons, aliphatic hydrocarbons, and mixtures thereof.
 18. The method of claim 17, wherein said aliphatic hydrocarbon is selected from the group consisting of C₁-C₆ aliphatic hydrocarbons and mixtures thereof.
 19. The method of claim 17, wherein said aliphatic hydrocarbons and mixtures thereof is comprised of primarily C₄ aliphatic hydrocarbons.
 20. The method of claim 17, wherein said fluid solvent consists essentially of C₄ liquefied petroleum gas.
 21. The method of claim 17, wherein said fluid solvent is n-butane, butane isomers, or mixtures thereof.
 22. The method of claim 1, wherein said temperature in the contacting, dissolving, settling and purification steps is from about 110° C. to about 170° C.
 23. The method of claim 1, wherein said pressure in the contacting step is from about 1,100 psig (7.58 MPa) to about 5,500 psig (37.92 MPa).
 24. The method of claim 1, wherein said pressure in the contacting is less than about 1,100 psig (7.58 MPa).
 25. The method of claim 1, wherein said pressure in the dissolving, settling, and purification steps is greater than about 4,500 psig (31.03 MPa).
 26. The method of claim 1, wherein said pressure in the dissolving, settling, and purification steps is greater than about 5,500 psig (37.92 MPa).
 27. The method of claim 1, wherein said solid media is selected from the group consisting of inorganic substances, carbon-based substances, and mixtures thereof.
 28. The method of claim 27, wherein said inorganic substances are selected from the group consisting of oxides of silicon, oxides of aluminum, oxides of iron, aluminum silicates, amorphous volcanic glasses, and mixtures thereof.
 29. The method of claim 27, wherein said inorganic substances are selected from the group consisting of silica gel, diatomite, sand, quartz, alumina, perlite, fuller's earth, bentonite, and mixtures thereof.
 30. The method of claim 27, wherein said carbon-based substances are selected from the group consisting of anthracite coal, carbon black, coke, activated carbon, cellulose, and mixtures thereof.
 31. The method of claim 1, wherein said contacting of the polyethylene solution with said solid media is done in a packed bed of said solid media.
 32. The method of claim 31, where said packed bed is greater than 20 cm in length. 